metadata.conference.dc.title: Characterization of Oxide Growth on Surface of Al-Mg-Si Welded Joint
metadata.conference.dc.contributor.*: Azman Jalar
Nur Azida Che Lah
Norinsan Kamil Othman
Roslinda Shamsudin
Abdul Razak Daud
Syed Roslee Sayd Bakar
(UniKL MFI) Feb-2014
metadata.conference.dc.publisher: Hindawi
metadata.conference.dc.identifier.citation: Azman Jalar, Nur Azida Che Lah, Norinsan Kamil Othman, Roslinda Shamsudin, Abdul Razak Daud, and Syed Roslee Sayd Bakar, “Characterization of Oxide Growth on Surface of Al-Mg-Si Welded Joint,” Advances in Materials Science and Engineering, vol. 2014, Article ID 272804, 10 pages, 2014. doi:10.1155/2014/272804
metadata.conference.dc.description.abstract: Al-Mg-Si (AA6061) Al alloy plates were joined by the method of gas metal arc welding using Al-5Mg (ER5356) filler metal and were subjected to the oxidation test in flowing air environment at from 8 to 40 hours and the weight gain was measured. The characteristic of oxide grown on welded zone surface was examined by SEM/EDS, XRD, and XPS. Oxide was observed to grow on the fused metal surface suggesting the possibility of modifying the oxide chemistry under high temperature environment. It was found that the oxidation behavior of fused metal affected by the nature of their oxide growth and morphology, was influenced by their welding process and the difference in the chemical composition.
metadata.conference.dc.description: Copyright © 2014 Author. This is an open access article distributed under the Creative Commons Attribution License, which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited.
metadata.conference.dc.identifier.uri: http://localhost/xmlui/handle/123456789/10244
Appears in Collections:Journal Articles

Files in This Item:
File Description SizeFormat 
Nur Azida_Characterization of Oxide Growth on Surface of Al-Mg-Si Welded Joint.pdf3.76 MBAdobe PDFView/Open

Items in UniKL IR are protected by copyright, with all rights reserved, unless otherwise indicated.