Electro-Discharge Machining of Zr67Cu11Ni10Ti9Be3: An Investigation on Hydroxyapatite Deposition and Surface Roughness

Abstract

This study attempts to simultaneously machine and synthesize a biomimetic nanoporous hydroxyapatite coating on the Zr67Cu11Ni10Ti9Be3 bulk metallic glass (BMG) surface. The aim is to investigate and optimize the hydroxyapatite deposition rate and the surface roughness during the electro-discharge coating of Zr67Cu11Ni10Ti9Be3 BMG. Scanning Electron Microscopy (SEM), X-ray powder Diffraction (XRD) and Energy-dispersive X-ray Spectroscopy (EDS) were employed to characterize and analyze the results. Response Surface Methodology using D-optimum custom design approach was utilized to generate the models and optimize the input parameters. A globule nanostructured and nanoporous coating of about 25.2 µm thick, containing mainly Ca, O, and K were ascertained. Further XRD analysis confirmed the deposition of biocompatible oxides (HA, CaZrO3, and ZrO2) and hard ZrC coating on the Zr67Cu11Ni10Ti9Be3 BMG surface. A significant improvement in cell viability was observed in the HA electro-discharge coated BMG specimens.